PostPosted: Fri Dec 29, 2017 6:03 pm 
Offline
Board Sponsor & SL6 Racer

Joined: Wed Oct 23, 2002 7:57 pm
Posts: 8284
Location: Waynesboro, Pa.
Car Model: 65 Valiant 2Dr Post
Help me understand too?

You acid clean before you go to the machine shop? Then when it comes back, is it ready for the Hard Block? Or does it need some other process to clean up the surface rust that they come back with. At least all of the ones I have picked up have surface rust.

Rick

_________________
2 Mopars come with Spark plug tubes. One is a world class, racing machine. The other is a 426 CI. boat anchor!
Image
12.70 @ 104.6
Image


Top
   
PostPosted: Fri Dec 29, 2017 7:50 pm 
Offline
Board Sponsor & Moderator
User avatar

Joined: Mon Oct 21, 2002 11:08 am
Posts: 16451
Location: Blacksburg, VA
Car Model:
Acid removes the rust, after you get the grease/oil off...

Lou

_________________
Home of Slant6-powered fun machines


Top
   
PostPosted: Fri Jan 11, 2019 2:34 pm 
Offline
1 BBL (New)

Joined: Sun Sep 02, 2018 4:49 pm
Posts: 7
Car Model: 1981 dodge colt 144.396mph record
Howdy,
I'm going to be rebuilding a slant6 at some point, and was reading up on various procedures,, this one caught my eye.. DD says something about needing to have the deck resurfaced after either acid dipping or the molasses treatment..
My question is... what about the machined surfaces of the bearings or any other machined surfaces? if you gotta do the deck surface why not those surfaces too? or was it that those were expected to be done and just not mentioned? thanks..

and... should I have started a new topic on this? instead of asking a question on / in an old topic? I was not sure what to do.. I'm sorry if I did it incorrectly, lemme know..

thanks.. drive carefully


Top
   
PostPosted: Fri Jan 11, 2019 4:54 pm 
Offline
Supercharged

Joined: Wed Sep 17, 2008 6:48 pm
Posts: 3805
Location: Indianapolis
Car Model:
I am thinking that the folks that wrote in this specific post are acid cleaning the water jackets to get maximum adhesion
when using a water jacket filler, necessary to stiffen the crankcase when pushing the limits on cylinder compression.

If you are doing a normal slant six rebuild, and if the water jackets are so corroded that they need acid cleaned, I would find a different
crankcase.

So yes, a new post listing your plans and expectations for the car-motor-rebuild would allow a better response.

_________________
Doo Ron Ron and the Duke of Earl are friends of mine.....
https://www.youtube.com/watch?v=uX8Nj8ABEI8


Top
   
PostPosted: Sat Jan 12, 2019 1:29 am 
Offline
Supercharged

Joined: Thu May 12, 2005 11:50 pm
Posts: 6291
Location: So California
Car Model: 64 Plymouth Valiant
The bearings are lined with bearing shells.

The deck is an actual sealing surface.

_________________
Ed
64 Valiant 225 / 904 / 42:1 manual steering / 9" drum brakes

8)


Top
   
PostPosted: Sat Jan 12, 2019 5:38 am 
Offline
1 BBL (New)

Joined: Sun Sep 02, 2018 4:49 pm
Posts: 7
Car Model: 1981 dodge colt 144.396mph record
I’m asking this question because I have not seen or touched the effects of acid cleaning a cast iron block, I’ve only seen the pics posted of a dirty then cleaned 4 cylinder block on this site. Probably, when I actually do the cleaning procedure the results will show me that it makes sense to just machine the deck and not the other machined surfaces. However, from a purely theoretical point, if the deck surface is damaged to the point that it does not seal, why do main bearing >supports< of the bearing shells not need machining also? I’m not trying to break anybodies chops, I think the answer to this question is important, if only to me.
Thanks drive careful


Top
   
PostPosted: Sat Jan 12, 2019 10:45 am 
Offline
Supercharged

Joined: Wed Sep 17, 2008 6:48 pm
Posts: 3805
Location: Indianapolis
Car Model:
the top of the block, just like the bottom of the head and like the manifold faces are important sealing surfaces.

if the surface finish is too rough ( pits - gouges) the gasket will not have the ability to fill in and seal those defects.


As stated the bearing seats have bearing inserts on top of them, they do not make a 'seal' of any kind.


You should also know that it is standard maching shop procedure to Hot Tank the block and head prior to any machine work.


Typically the hot tank cleaning process will get the parts clean down to the metal..


Check out how well your chosen machine shop can clean your parts then see if any additional treatment is necessary.

_________________
Doo Ron Ron and the Duke of Earl are friends of mine.....
https://www.youtube.com/watch?v=uX8Nj8ABEI8


Top
   
PostPosted: Fri Feb 08, 2019 8:08 am 
Offline
2 BBL ''SuperSix''

Joined: Sat Dec 13, 2008 11:54 am
Posts: 20
Location: SOCAL
Car Model:
Doctor Dodge wrote:
We have cleaned a lot of parts over the years, using many different chemicals and processes...
For being the nasty process it is, the pool acid treatment seems to work the best when it comes to getting the water jackets totally clean, with-out spending a lot of time or money.

We do the "acid soak" right after engine break-down and then send the engine into the shop for their "cleaning" / machining. ( hot tank, baking, "dishwasher" or what-ever they like to use...)
When we pick the parts up, the shop usually asks me: " How did you get the water jackets so clean?" :wink: :lol:

One other side note, the acid etching can help you find cracks. The acid gets into the cracks, then bleeds-out and leaves stains, if let the block dry completely, after the etching process.
DD

Image

what do you recommend for aluminum blocks?


Top
   
PostPosted: Sun Feb 10, 2019 12:47 pm 
Offline
Guru
User avatar

Joined: Sat Oct 12, 2002 11:22 am
Posts: 3740
Location: Sonoma, Calif.
Car Model: Many Darts and a Dacuda
Bead Blasting.
DD


Top
   
Display posts from previous:  Sort by  
Post new topic  Reply to topic  [ 24 posts ]  Go to page Previous 1 2

All times are UTC-07:00


Who is online

Users browsing this forum: Bing [Bot] and 59 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  
Powered by phpBB® Forum Software © phpBB Limited